SPINDLE TAPES

 
 

UNMATCHED
CHARACTERISTICS

 

UNBEATABLE RESULTS

Light Weight & High Flexibility.
High Strength & High Elasticity.
High Coefficient of Friction on drum side  High Abrasion Resistance Permanently Antistatic Quick Splicing and Jointing.

SPINDLE TAPES

Saving in Power Consumption up to 14 % uniform Spindle Speed & Excellent yarn Quality. Low idle spindlage - Higher productivity Quick acceleration to required speed. Braking a spindle does not affect adjacent spindles No accumulation of fluff, Minimum downtime of machine.

 

PROPERTIES

Light Weight & high Flexibility.
High Strength & High Elasticity
High Coefficient of Friction on drum side.
High abrasion Resistance.
permanently Antistatic.
Quick Splicing and Joining of Spindle Tapes.

 

ADVANTAGES

Saving in Power Consumption up to 14%.
uniform Spindle Speed & Excellent Yarn Quality.
Low idle spindlage - High productivity.
Quick acceleration to required speed.
Braking a spindle does not affect adjacent spindle.
no accumulation of fluff. Minimum downtime of machines.

 

PREPARATION:

1 Grind to given Length of Joint ( 20 mm for KHST-5 & 25 mm for KHST-80) with grinding machine.
2 Clean & adjust the part of joint Knife to remove the loose particles of Rubber etc.
3 Apply a thin coat of Adhesive to skived area of both ends and allow it to dry until slightly sticky.
4 position both ends correctly in pre-heated ( at 70șc ) Press.
5 Leave Joint in press for a minimum of 3 minutes in case of SR-5 & 10 minutes in case of ST-80 under heat & Pressure.
6 Switch off power & allow the joint to cool under pressure.
  Tension must not be applied before Joint is completely cool.
 
 

TECHNICAL PARAMETERS

 

KHST-5

KHST-51

KHST-80

Thickness

0.55mm

0.60

0.80mm

Breaking Strength

75Kg/Cm

8.5kg

95kg/Cm.

Elongation at Break

20%

18%

18%

Surface
Cylinder Side

Elastomer coated Polyamide Fabric

18%

Elastomer Coated Polyamide Fabric
Wharves Side Blend of Cotton & Polyamide Fabric

18%

Blend of Cotton & Polyamide Fabric
Coefficient of Friction
Cylinder Side
0.55

18%

0.55
Wharves Side 0.28 0.28
   